Ceramic Fiber Module
Ceramic Fiber Module is made of blanket fan folded, or pre-cut blanket stack bonded to form a module, to form a module with cut edges exposed. It's an ideal refractory material for high temperature industry.
SEND EMAIL CHAT NOW
Ceramic Fiber Module for Hith Temperature Insulation & Refractory
Ceramic Fiber Module is made of creamic fiber blanket fan folded, or pre-cut blanket stack bonded to form a module, to form a module with cut edges exposed. It's an ideal refractory material for high temperature industry.
CHARACTERISTIC
Low density and low thermal conductivity
To be secured by concealed anchor
Greater mechanical strength
Shorter heat up and cool down time
Resilience and resistance to thermal shock
Flexible and easy to cut or install
Asbestos free
APPLICATIONS
 |
|
TECHNICAL DATA
Blanket Product |
MCF1050 |
MCF1260ST |
MCF1260HP |
MCF1300HA |
MCF1300LAZS |
MCF1430AZS |
Temperature Grade°C |
1050 |
1260 |
1260 |
1300 |
1300 |
1430 |
Recommended Operation Temperature°C |
≤950 |
≤1100 |
≤1150 |
≤1200 |
≤1200 |
≤1250 |
Product Code |
MYTX-PT-02 |
MYTX-BZ-02 |
MYTX-GC-02 |
MYTX-GL-02 |
MYTX-DG-02 |
MYTX-HG-02 |
Permanent Linear Shrinkage (%) |
950°C×24h≤4 |
1000°C×24h≤4 |
1100°C×24h≤4 |
1200°C×24h≤4 |
1250°C×24h≤4 |
1350°C×24h≤4 |
Nominal Density (kg/m3) |
180~240 |
|||||
Al2O3 |
≥40 |
≥43 |
≥44 |
≥52 |
||
Al2O3+SiO2 |
≥95 |
≥97 |
≥98.5 |
≥98.5 |
||
Al2O3+SiO2+ZrO2 |
- |
- |
≥99 |
≥99 |
||
ZrO2 |
- |
- |
5~7 |
≥15 |
||
Fe2O3 |
≤1.0 |
≤1.0 |
≤1.0
|
≤1.0
|
≤0.5 |
≤0.5 |
Availability (mm) |
Per customer’s drawing |
|||||
Note: Test data shown are average results of tests conducted under standard procedures and are subject to variation. Results should not be used for specification purpose. The product is listed comply to ASTM C892.