Ceramic Fiber Blanket
Ceramic Fiber Blanket is made of high purity Alumino-Silicate (and Zirconia) fibrous wool.
SEND EMAIL CHAT NOWCeramic Fiber Blanket for High Temperature Insulation & Refractory
Ceramic Fiber Blanket is made of high purity Alumino-Silicate (and Zirconia) fibrous wool. It's one of the best choices for high temperature insulation and refractory.
CHARACTERISTIC
Needled blanket
Non-combustible
Low density and low thermal conductivity
Shorter heat up and cool down time
Resilience and resistance to thermal shock
Contain no organic binder
Asbestos free
APPLICATIONS
 |
|
TECHNICAL DATA
Blanket Product |
MCF1050 |
MCF1260ST |
MCF1260HP |
MCF1300HA |
MCF1300LAZS |
MCF1430AZS |
||
Temperature Grade°C |
1050 |
1260 |
1260 |
1300 |
1300 |
1430 |
||
Recommended Operation Temperature°C |
≤950 |
≤1100 |
≤1150 |
≤1200 |
≤1200 |
≤1250 |
||
Permanent Linear Shrinkage (%) |
950°C×24h≤4 |
1000°C×24h≤4 |
1100°C×24h≤4 |
1200°C×24h≤4 |
1250°C×24h≤4 |
1350°C×24h≤4 |
||
Thermal Conductivity (Mean Temp 500°C) W/(m·k) |
≤0.153 |
|||||||
Short Content (ф≥0.212mm) (%) |
≤20 |
≤20 |
≤20 (Kaolin) |
≤15 （HP） |
≤20 (Kaolin) |
≤15 （HP） |
≤15 |
≤15 |
Tensile Strength (for 25mm thickness blanket) (MPa) |
≥0.04 |
|||||||
Nominal Density (kg/m3) |
64/96/128/160 |
|||||||
Al2O3 |
≥40 |
≥43 |
≥44 |
≥52 |
||||
Al2O3+SiO2 |
≥95 |
≥97 |
≥98.5 |
≥98.5 |
||||
Al2O3+SiO2+ZrO2 |
≥99 |
≥99 |
||||||
ZrO2 |
5~7 |
≥15 |
||||||
Fe2O3 |
≤1.0 |
≤1.0 |
≤1.0 (Kaolin) |
≤0.5 (HP) |
≤1.0 (Kaolin) |
≤0.5 (HP) |
≤0.5 |
≤0.5 |
Availability (Standard Product) |
T: 6mm~60mm; W: 610mm/1220mm; L: 7320mm/7620mm for 25mm thickness (3810mm for 50mm T; 5490mm for 38mm T) |
|||||||
Note: Test data shown are average results of tests conducted under standard procedures and are subject to variation. Results should not be used for specification purpose. The product is listed comply to ASTM C892.